Casting Schedules?
Moderator: Brad Walker
-
- Posts: 151
- Joined: Sun Mar 09, 2003 5:42 pm
- Location: Greensboro NC
- Contact:
Casting Schedules?
Is there a website (besides BE) that has annealing schedules for large, thick castings? Especially interested in float glass.
-
- Posts: 2339
- Joined: Tue Mar 11, 2003 12:06 am
- Location: Chatham NH
- Contact:
Re: Casting Schedules?
Get the book, Firing Schedules for Glass by StoneBarbara Cashman wrote:Is there a website (besides BE) that has annealing schedules for large, thick castings? Especially interested in float glass.
Bert
Bert Weiss Art Glass*
http://www.customartglass.com
Furniture Lighting Sculpture Tableware
Architectural Commissions
Bert Weiss Art Glass*
http://www.customartglass.com
Furniture Lighting Sculpture Tableware
Architectural Commissions
Re: Casting Schedules?
Dear Bert
In the book, are there firing schedules only for float glass or are there schedules to adapt also to BE or other glass?
I would buy me the book, but never used float till now.
Thank you
In the book, are there firing schedules only for float glass or are there schedules to adapt also to BE or other glass?
I would buy me the book, but never used float till now.
Thank you
Re: Casting Schedules?
Yes, there are schedules for many glasses in the book.
-
- Posts: 2339
- Joined: Tue Mar 11, 2003 12:06 am
- Location: Chatham NH
- Contact:
Re: Casting Schedules?
Many of the main schedules are written for float, and there is a chart for adapting to other glasses. Bullseye Tested Compatible and System 96 use the same anneal schedules. Stone is good at explaining the why's of what he suggests.la suisse wrote:Dear Bert
In the book, are there firing schedules only for float glass or are there schedules to adapt also to BE or other glass?
I would buy me the book, but never used float till now.
Thank you
Do understand that there is not only one way to accomplish an anneal for glass, especially considering that we control based on air temperature and not glass temperature. I have float schedules that I devised based on info I got from a glass engineer at PPG. My schedules use about the same amount of time as Stone's, which makes sense to me. However, I soak longer at a lower temperature than Stone does. He has a short soak at a higher temperature, followed by a slow ramp down. I once asked Dan and Ray, both founders of Bullseye, about the difference in strategies. To my surprise they liked my approach better. Several years later, they revised the Bullseye anneal schedules for thick glass castings. So, applying the paradigm used by Stone, I add 80ºF to Bullseye's schedules to get one for float. Sometimes these schedules go a bit faster than mine, and they seem to work OK, if I am in a rush. Bullseye did extensive testing and research to devise their schedules. They got a recording pyrometer with 6 thermocouple inputs. 3 were in the air and one beneath the glass, one in the core of the glass, and one on the glass surface. What they were looking for was the time it took at a particular air temperature for the 3 thermocouples in the glass to equalize. Annealing takes place when the entire mass of glass is within 5ºC, inside the annealing range. Once this happens, it is only a matter of seconds for the stresses to be relieved. (BTW, you can make thermocouples by welding very thin specific wires at their tips. Fortunately these wires have a higher COE than glass, so the glass remains intact during these tests.)
So, for me, I often look at Stone, Bullseye, and my own charts to decide where to go with annealing. Be very aware that these charts are all assuming uniform thickness for the glass. When you have thick and thin spots, within the glass, it takes longer to get the different sections to equalize within the range. Also be aware that if your kiln has uneven temperatures inside it, the longer you hold the glass in that environment, the more those gradients are transferred to the glass. If the difference in the glass is greater than 5ºC, it CAN NOT anneal. There is a sweet spot between too long and too short, where it can work just fine.
Bert
Bert Weiss Art Glass*
http://www.customartglass.com
Furniture Lighting Sculpture Tableware
Architectural Commissions
Bert Weiss Art Glass*
http://www.customartglass.com
Furniture Lighting Sculpture Tableware
Architectural Commissions